Influences of Ytterbium on Microstructure and Properties of BAg30 Filler Metals and Brazed Joints
Author:
Affiliation:

1.Zhengzhou Research Institute of Mechanical Engineering Co., Ltd, Zhengzhou 450001, China;2.School of Mechatronic Engineering, Jiangsu Normal University, Xuzhou 221116, China

Fund Project:

Major State Research Development Program of China (2019YFF0217400); Central Plains Science and Technology Innovation Leading Talents Program (ZYQR20180030)

  • 摘要
    • | |
  • 访问统计
    • |
  • 参考文献 [15]
    • |
  • 相似文献 [20]
    • | | |
  • 文章评论
    摘要:

    研究了Yb元素对Ag30-Cu-Zn-Sn（BAg30）钎料热性能、润湿性和微观组织的影响，分析了焊点的剪切强度和断口形貌，优化了钎料组分。结果表明，BAg30钎料添加1%（质量分数，下同）Yb后可以显著降低钎料液相线-固相线差值，促进钎料在钢基板表面的润湿性，细化微观组织。然而，当Yb添加量超过1%后，过量的Yb元素会降低钎料的性能，粗化微观组织。通过焊点剪切测试，BAg30-1% Yb钎料的焊点抗剪切强度和断裂形貌表现出明显的优越性，抗剪切强度相较于BAg30钎料焊点明显提高，断口形貌出现均匀细小的韧窝，表现为韧性断裂机制。

    Abstract:

    The effects of ytterbium (Yb) on the thermal behavior, wettability, and microstructures of Ag30-Cu-Zn-Sn (BAg30) filler metals were investigated. The shear strength and fracture morphology of brazed joints were analyzed to optimize the filler composition. Results reveal that the addition of 1wt% Yb in BAg30 filler metal can significantly decrease the temperature difference between solidus temperature and liquidus temperature, improve the wettability of filler on the steel substrate, and refine the microstructures. However, the excessive addition of Yb (more than 1wt%) can degrade the properties and coarsen the microstructure. According to the shear strength tests, the BAg30-1wt% Yb brazed joint shows obvious superiority in shear strength and fracture morphology: its shear strength is higher than that of the original BAg30 brazed joint, and the fracture mechanism is ductile fracture, presenting the homogeneous and fine dimples.

    参考文献
    [1] Kaiwa K, Yaoita S, Sasaki T et al. Advanced Materials Research[J], 2014, 922: 322
    [2] Pu Juan, Zhang Lei, Wu Mingfang et al. Transactions of the China Welding Institution[J] 2021, 42(1): 58 (in Chinese)
    [3] Ma C L, Xue S B, Wang B. Journal of Alloys and Compounds[J], 2016, 688: 854
    [4] Zhang G W, Bao Y F, Jiang Y F et al. Journal of Materials Engineering and Performance[J], 2011, 20: 1451
    [5] Xiong M Y, Zhang L. Journal of Materials Science[J], 2019, 54(2): 1741
    [6] Li Z R, Cao J, Liu B et al. Science & Technology of Welding and Joining[J], 2010, 15(1): 59
    [7] Ma C L, Xue S B, Wang B et al. Journal of Materials Engineering and Performance[J], 2017, 26(7): 3180
    [8] Lai Zhongmin, Wang Jianxin, Lu Fangyan. Transactions of the China Welding Institution[J], 2011, 32(1): 9 (in Chinese)
    [9] Lai Z M, Xue S B, Han X P et al. Rare Metal Materials and Engineering[J], 2010, 39(3): 397
    [10] Lu Fangyan. Thesis for Doctorate[D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2010 (in Chinese)
    [11] Zhang Liang, Yang Fan, Guo Yonghuan et al. Chinese Rare Earths[J], 2017, 38(5): 33 (in Chinese)
    [12] Zhang L, Fan X Y, Guo Y H et al. Materials and Design[J], 2014, 57(5): 646
    [13] Cao J, Zhang L X, Wang H Q et al. Journal of Materials Science and Technology[J], 2011, 27(4): 377
    [14] Zhang L. Journal of Manufacturing Processes[J], 2021, 66: 651
    [15] Zhang L, Liu Z Q. Journal of Materials Science: Materials in Electronics[J], 2020, 31(3): 2466
    引证文献
    网友评论
    网友评论
    分享到微博
    发 布
引用本文

张亮,钟素娟,董宏伟,王蒙,龙伟民.Yb元素对BAg30硬钎料及焊点组织与性能的影响[J].稀有金属材料与工程,2022,51(7):2344~2348.[Zhang Liang, Zhong Sujuan, Dong Hongwei, Wang Meng, Long Weimin. Influences of Ytterbium on Microstructure and Properties of BAg30 Filler Metals and Brazed Joints[J]. Rare Metal Materials and Engineering,2022,51(7):2344~2348.]
DOI：10.12442/j. issn.1002-185X. E20210532

复制
文章指标
  • 点击次数:361
  • 下载次数: 940
  • HTML阅读次数: 198
  • 引用次数: 0
历史
  • 收稿日期:2021-06-22
  • 最后修改日期:2021-08-18
  • 录用日期:2021-09-01
  • 在线发布日期: 2022-08-03
  • 出版日期: 2022-07-27

总访问量 36847558

地址：西安市未央区未央路96号 邮政编码：710016 联系电话：029－86231117

E-mail：rmme@c-nin.com; rmme0626@aliyun.com

版权所有:稀有金属材料与工程 ® 2025 版权所有 技术支持:北京勤云科技发展有限公司 ICP:陕ICP备05006818号-3