Ti-22Al-25Nb合金热机械处理组织与性能研究
DOI:
作者:
作者单位:

钢铁研究总院高温材料研究所,钢铁研究总院高温材料研究所,钢铁研究总院高温材料研究所,西北工业大学材料学院 凝固技术国家重点实验室

作者简介:

通讯作者:

中图分类号:

基金项目:


Research of microstructure and mechanical properties of Ti-22Al-25Nb alloy during hot mechanical processing
Author:
Affiliation:

High Temperature materials Research Institute,Central Iron and Steel Research Institute,High Temperature materials Research Institute,Central Iron and Steel Research Institute,High Temperature materials Research Institute,Central Iron and Steel Research Institute,School of Materials Science and Engineering,Northwestern Polytechnical University,Xi’an

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文研究了Ti-22Al-25Nb合金的显微组织和力学性能,重点介绍了等温锻造温度、固溶时效处理对合金力学性能的影响规律。结果表明:随着等温锻造温度的升高,合金的强度和塑性先增加后降低。在O+B2两相区固溶时,随着固溶温度的升高,具有较高塑性的B2相体积分数的增加和等轴颗粒的减少是合金具有较高塑性的主要原因;而在α2+B2+O三相区固溶时,片层厚度的减小有利于合金强度的提高,但过大的B2相晶粒尺寸和较细的片层厚度则对合金的塑性不利。相的含量、形态、尺寸对合金力学性能的影响较大,尽可能在B2相变点附近进行等温锻造,以控制等轴颗粒数量和B2相晶粒尺寸,在低温时效以获得较细的片层组织从而提高合金的强度和塑性。

    Abstract:

    The microstructure and mechanical property of the Ti-22Al-25Nb is investigated and the effects of the forging, solution and aging temperature on the mechanical properties are introduced. As the isothermal forging temperature increases, the strength and ductility of the alloy increases at first and then decreases. When solution conducted in O+B2 region, as the solution temperature increases, the increasing B2 volume and decreasing particle are the main reason for high ductility of the alloy. When solution conducted in α2+B2+O region, the decrease of lamellar thickness is beneficial for the strength while the large B2 grain size and fine lamella are harmful for the ductility. The phase volume, morphology and size have significant influence on the mechanical properties of the alloy. A basic principle to improve the tensile property of the alloy is isothermal forging nearby the B2-transus in order to control the amount of the particle and the B2 grain size, and followed by low temperature aging to obtain fine lamella.

    参考文献
    相似文献
    引证文献
引用本文

马 雄,张建伟,梁晓波,曾卫东. Ti-22Al-25Nb合金热机械处理组织与性能研究[J].稀有金属材料与工程,2017,46(5):1375~1379.[Ma Xiong, Zhang Jianwei, Liang Xiaobo, Zeng Weidong. Research of microstructure and mechanical properties of Ti-22Al-25Nb alloy during hot mechanical processing[J]. Rare Metal Materials and Engineering,2017,46(5):1375~1379.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-05-09
  • 最后修改日期:2016-06-22
  • 录用日期:2016-07-04
  • 在线发布日期: 2017-09-27
  • 出版日期: