Study of Compressive Twinning Behavior in High-purity Titanium
Author:
Affiliation:

Chongqing University,,,

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    利用背散射电子衍射(EBSD)技术对高纯钛形变组织中{11-22}和{11-24}压缩孪生进行了研究。结果表明:{11-24}孪晶总是伴随{11-22}孪晶在同一晶粒中产生,在变形组织中没有发现单独存在的{11-24}孪晶;这种极少出现的{11-24}压缩孪晶主要由{11-22}孪晶与晶界或{11-22}孪生变体之间交互作用改变了局部应力状态而诱发的。由{11-22}孪晶诱发的{11-24}孪晶更倾向于同其中一个{11-22}孪生变体具有相同的转轴。此外,根据晶体对称性及相同晶粒中{11-22}和{11-24}孪晶之间的取向关系,{11-22}-{11-24}孪晶反应可形成四种不同类型的孪晶反应界面。

    Abstract:

    Compressive twinning behavior in high-purity titanium was studied by electrical back-scattered diffraction (EBSD) techniques. The results show that {11-24} twins are always accompanied with {11-22} twins in some specific grains, and individual {11-24} twin is not observed in microstructure of the deformed sample. The formation of {11-24} twin is attributed to the changes of local stress states, which induced by the {11-22}-{11-22} twin variants interactions or {11-22} twin interactes with the grain boundaries. The {11-22} and {11-24} twins tend to share a common rotation axis with one of the {11-22} twin variant within an initial grain. In addition, due to the crystal symmetry and the orientation relationships between {11-22} and {11-24} twins, interactions between {11-22} and {11-24} twins inevitably occur, which results in four different types of {11-22}-{11-24} twin junctions.

    参考文献
    相似文献
    引证文献
引用本文

任 毅,张喜燕,孙 奇,刘 庆.高纯钛压缩孪生行为研究[J].稀有金属材料与工程,2018,47(7):2061~2066.[Ren Yi, Zhang Xiyan, Sun Qi, Liu Qing. Study of Compressive Twinning Behavior in High-purity Titanium[J]. Rare Metal Materials and Engineering,2018,47(7):2061~2066.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-09-02
  • 最后修改日期:2016-12-28
  • 录用日期:2017-02-21
  • 在线发布日期: 2018-10-10
  • 出版日期: