镍基变形高温合金中g′ 相的多尺度分布行为及其对热变形性能的影响
DOI:
作者:
作者单位:

1.上海交通大学;2.中国航发商用航空发动机有限责任公司

作者简介:

通讯作者:

中图分类号:

基金项目:

Aerospace Support Fund (Grant No. 15GFZ-JJ20-04), the Industry-University-Research Cooperation Annual Plan of Shanghai under Project No. CXY-2016-004 and China Postdoctoral Science Foundation 17Z102060125


Multimodal distribution of g′ phase and effect on hot deformation in a wrought nickel base superalloy
Author:
Affiliation:

Shanghai Jiao Tong University

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文主要研究了镍基变形高温合金在不同热处理过程中g′相的析出、形貌、尺寸及分布行为。通过扫描电镜观察分析高温固溶热处理后连续冷却、中断固溶冷却以及等温时效淬火后的组织构成。研究结果表明,固溶处理后连续冷去过程中,当冷却速率较高时,二次g′尺寸大小均匀,呈现单峰分布,随着冷却速率降低,二次g′尺寸增加,逐渐聚集长大并呈现花状形貌;当等温时效过程中二次g′周围过冷度重新建立,随后淬火过程中会产生三次g′,三次g′与二次g′构成双峰分布。在此基础上,探讨了g′相析出及演化对合金热变形行为的影响。

    Abstract:

    The microstructural evolution of different generations of ?′ precipitates during various heat treatment processes of a nickel base superalloy has been investigated. After solutionizing in the single ? phase field, continuous cooling, interrupted cooling and isothermal annealing tests were performed and characterization of the precipitates was carried out by scanning electron microscopy. It is found that a monomodal size distribution of the secondary ?′ precipitates can be achieved at a very high cooling rate in the continuous cooling process. With the decrease of the cooling rate, the secondary ?′ precipitates grow gradually and gather together to form a flowery morphology. When the secondary supersaturation is developed in the vicinity of the secondary ?′ precipitates during isothermal annealing, the water-quenched tertiary ?′ precipitates are produced and result in a bimodal size distribution of ?′ precipitates with the larger secondary precipitates. Furthermore, the effects of the secondary ?′ particle growth on the hot deformation are also discussed.

    参考文献
    相似文献
    引证文献
引用本文

韩国明,李飞,陈晓燕,李玉龙,王飞,汪东红,孙宝德.镍基变形高温合金中g′ 相的多尺度分布行为及其对热变形性能的影响[J].稀有金属材料与工程,2019,48(9):2821~2828.[Han Guoming, Li Fei, Chen Xiaoyan, Li Yulong, Wang Fei, Wang Donghong, Sun Baode. Multimodal distribution of g′ phase and effect on hot deformation in a wrought nickel base superalloy[J]. Rare Metal Materials and Engineering,2019,48(9):2821~2828.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2018-04-16
  • 最后修改日期:2018-10-22
  • 录用日期:2018-11-08
  • 在线发布日期: 2019-10-09
  • 出版日期: