高温变形条件下5A02铝合金的塑性成形性能
DOI:
作者:
作者单位:

1.机械电子工程学院 南京林业大学;2.燕山大学机械工程学院;3.山东科技大学机电学院

作者简介:

通讯作者:

中图分类号:

基金项目:

国家自然科学基金面上项目(51775480);江苏省教育厅高等学校自然科学积极面上项目(18KJB460020), 南京林业大学高学历人才启动基金(GXL2018020);南京林业大学青年创新基金(CX2018027).


The plastic deformation behavior of 5A02 aluminum alloy sheet at high temperature
Author:
Affiliation:

1.College of Mechanical and Electronic engineering,Nanjing Forestry University;2.School of Mechanical Engineering,Yanshan University;3.College of Mechanical and Electronic Engineering,Shandong University of Science and Technology

Fund Project:

National Natural Science Foundation of China (51775480), Natural Science Foundation of Jiangsu Higher Education Institutions of China(18KJB460020), High-level (Higher education) Science Foundation of Nanjing Forestry University(GXL2018020) and the Youth Science and Technology Innovation Foundation of Nanjing Forestry University(CX2018027).

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    随着工业技术的发展和能源问题的突出,铝合金以其质量轻、耐腐蚀性能好、成形性能和加工性能良好等优势成为轻型化首选的材料类型之一。以5A02铝合金冷轧板材为研究对象,通过单向拉伸试验和金相试验对不同变形温度、应变速率条件下5A02铝合金的塑性性能进行分析,并且借助试验数据和Zener-Hollomo参数模型,对高温条件下5A02铝合金的本构模型进行研究。研究结果表明:5A02铝合金在高温条件下变形时,应变速率和变形温度对延伸率的影响很大。在应变速率为0.01s-1、0.001 s-1、0.0005 s-1和0.0001 s-1条件下,当变形温度大于250℃时,5A02铝合金的延伸率大于100%。当变形温度为150℃~250℃时,5A02铝合金的真实应力-应变曲线属于动态回复型,而当变形温度大于250℃时,流变应力曲线存在明显的软化现象。

    Abstract:

    With the development of industrial technology and the rising of energy issues, aluminum alloys have become one of the preferred lightening materials for low weight, good corrosion resistance, good forming and processing properties. Taking 5A02 aluminum alloy cold-rolled sheet as the research object, the plastic deformation behavior of 5A02 aluminum alloy under different temperatures and strain rates were analyzed through uniaxial tensile test and metallographic test. Combined with experimental data and Zener-Hollomon parameter model, the constitutive model of 5A02 aluminum alloy under high temperature conditions was studied. The results show that the strain rate and deformation temperature have a great influence on the elongation when the 5A02 aluminum alloy is deformed under high temperature conditions. At strain rates of 0.01s-1, 0.001s-1, 0.0005s-1 and 0.0001s-1, the elongation of 5A02 aluminum alloy is greater than 100% when the deformation temperature is above 250°C. The true stress-strain curve of 5A02 aluminum alloy is characterized by dynamic recovery when the deformation temperature is 150°C~250°C, and the flow stress curve has obvious softening phenomenon when the deformation temperature is above 250°C.

    参考文献
    相似文献
    引证文献
引用本文

贾向东,袁荣娟,何留洋,曹秒艳,王瑞,赵长财.高温变形条件下5A02铝合金的塑性成形性能[J].稀有金属材料与工程,2020,49(7):2189~2197.[Xiang-dong Jia, Rong-juan Yuan, Liu-yang He, Miao-yan Cao, Rui Wang, Chang-cai Zhao. The plastic deformation behavior of 5A02 aluminum alloy sheet at high temperature[J]. Rare Metal Materials and Engineering,2020,49(7):2189~2197.]
DOI:[doi]

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-12-10
  • 最后修改日期:2020-05-26
  • 录用日期:2020-02-20
  • 在线发布日期: 2020-08-31
  • 出版日期: