Mechanical and Damping Properties of Porous Mg97Zn1Y2 Composites
Author:
Affiliation:

School of Materials Science and Engineering, East China Jiaotong University, Nanchang 330013, China

Fund Project:

National Natural Science Foundation of China (51665012); Jiangxi Province Science Foundation for Outstanding Scholarship (20171BCB23061, 2018ACB21020); Primary Research & Development Plan of Jiangxi Province (2019BBEL50019)

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    多孔材料是一种新型轻质的结构-功能材料,具有较高的阻尼性能,同时兼具密度小、质量轻等特点,使其具有广阔的应用价值。基于此,选取含有长周期特殊结构相(LPSO相)的Mg97Zn1Y2为基体,以MgCO3为发泡剂,SiC为增粘剂,通过熔体发泡法制备出镁基多孔材料,通过OM、SEM、TEM、XRD及DMA等技术手段,研究多孔Mg97Zn1Y2材料的力学性能、阻尼性能等。结果表明,多孔Mg97Zn1Y2材料主要由镁基体(α-Mg)、LPSO相和SiC相组成,当应变幅值较小时,多孔Mg97Zn1Y2复合材料的阻尼值明显优于Mg97Zn1Y2合金,随着孔隙率的增加,阻尼性能得到改善。孔隙率的增加降低了多孔Mg97Zn1Y2复合材料的抗压缩性能。此外,除了Mg97Zn1Y2合金本身的位错阻尼、界面阻尼和晶界阻尼之外,还有“气相”阻尼,共同影响着多孔Mg97Zn1Y2材料的阻尼性能。

    Abstract:

    Porous material is a new type of lightweight structure-functional material with high damping performance, low density, light weight, and other characteristics, making it useful in many applications. Mg97Zn1Y2 with long-period stacking ordered phase (LPSO phase) as a matrix, MgCO3 as foaming agent and SiC as tackifier was used to prepare magnesium-based porous materials by melt-foaming method. The mechanical properties and damping properties of the porous Mg97Zn1Y2 were studied by OM, SEM, XRD and DMA technology. Results show that the porous Mg97Zn1Y2 composites are mainly composed of magnesium matrix (α-Mg), LPSO phase and SiC phase. When the strain amplitude is small, the damping value of porous Mg97Zn1Y2 composites is obviously better than that of Mg97Zn1Y2 alloy, and the damping properties are improved as porosity is increased. However, increased porosity decreases the compression properties of porous Mg97Zn1Y2 composites. In addition to the dislocation damping, interface damping, and grain boundary damping of the Mg97Zn1Y2 alloy, “gas phase” damping is found to affect the damping properties of the porous Mg97Zn1Y2 composites jointly.

    参考文献
    相似文献
    引证文献
引用本文

万迪庆,韩国梁,王厚彬,胡佳俊,薛雁丹,董少云,王玉,汤浩,杨帆.多孔Mg97Zn1Y2材料的力学性能与阻尼性能[J].稀有金属材料与工程,2022,51(10):3626~3631.[Wan Diqing, Han Guoliang, Wang Houbin, Hu Jiajun, Xue Yandan, Dong Shaoyun, Wang Yu, Tang Hao, Yang Fan. Mechanical and Damping Properties of Porous Mg97Zn1Y2 Composites[J]. Rare Metal Materials and Engineering,2022,51(10):3626~3631.]
DOI:10.12442/j. issn.1002-185X.20210828

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2021-09-17
  • 最后修改日期:2021-11-15
  • 录用日期:2021-12-07
  • 在线发布日期: 2022-10-31
  • 出版日期: 2022-10-28