Optimal Duration Selection of Solid Solution Heat Treatment of Ni-based Single Crystal Superalloys Based on Statistical Analysis
Author:
Affiliation:

1.Shi Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;2.School of Materials Science and Engineering, University of Science and Technology of China, Shenyang 110016, China

Clc Number:

Fund Project:

National Key R&D Program of China (2021YFB3700400); National Science and Technology Major Project (2017-VI-0003-0073)

  • Article
  • |
  • Figures
  • |
  • Metrics
  • |
  • Reference
  • |
  • Related
  • |
  • Cited by
  • |
  • Materials
  • |
  • Comments
    Abstract:

    A novel approach was developed to select the optimal duration for solid solution heat treatment of Ni-based single-crystal (SX) superalloys based on the statistical analysis of γ′ phase size in the second-generation SX superalloys. The microstructure uniformity ω was introduced through the statistical analysis. The ω curves can be divided into three stages according to the statistical analysis: the significant change area, transition area, and steady state area. The transition area shows the optimal duration range for solution heat treatment of Ni-based SX superalloys. This approach was verified by measuring the γ′ rafting rate and testing the creep properties of alloys. Meanwhile, the accuracy of this approach was also validated through the fourth-generation Ni-based SX superalloys. This approach can effectively optimize the heat treatment and provide guidance for the design and engineering applications of SX superalloys.

    Reference
    Related
    Cited by
Get Citation

[Yunling Du, Yanhong Yang, Yizhou Zhou. Optimal Duration Selection of Solid Solution Heat Treatment of Ni-based Single Crystal Superalloys Based on Statistical Analysis[J]. Rare Metal Materials and Engineering,2022,51(9):3133~3137.]
DOI:10.12442/j. issn.1002-185X.20210793

Copy
Article Metrics
  • Abstract:
  • PDF:
  • HTML:
  • Cited by:
History
  • Received:September 07,2021
  • Revised:February 22,2022
  • Adopted:February 25,2022
  • Online: September 30,2022
  • Published: September 27,2022